Multifunctional halloysite and hectorite catalysts for effective transformation of biomass to biodiesel
2023
Halloysite surface was modified with tetrabutylammonium iodide, and then the obtained nanomaterial was used as support for ZnO nanoparticles. After characterization, the nanomaterial was used as a catalyst for fatty acid methyl esters (FAMEs) production. The recyclability of the nanomaterial was also investigated, and the optimization of reaction conditions by the design of experiments approach was performed as well. In addition, the synthesized nanomaterial was tested as a catalyst for FAME production from a series of waste lipids affording biodiesel in moderate to good yields (35–95%), depending on the matrix. To fully exploit the feasibility of clay minerals as catalysts in biodiesel for…
Luminescence mechanisms of defective ZnO nanoparticles.
2016
ZnO nanoparticles (NPs) synthesized by pulsed laser ablation (PLAL) of a zinc plate in deionized water were investigated by time-resolved photoluminescence (PL) and complementary techniques (TEM, AFM, μRaman). HRTEM images show that PLAL produces crystalline ZnO NPs in wurtzite structure with a slightly distorted lattice parameter a. Consistently, optical spectra show the typical absorption edge of wurtzite ZnO (Eg = 3.38 eV) and the related excitonic PL peaked at 3.32 eV with a subnanosecond lifetime. ZnO NPs display a further PL peaking at 2.2 eV related to defects, which shows a power law decay kinetics. Thermal annealing in O2 and in a He atmosphere produces a reduction of the A1(LO) Ra…
Synthesis of multi-color luminescent ZnO nanoparticles by ultra-short pulsed laser ablation
2020
Abstract Crystalline ZnO nanoparticles (NPs) are synthesized by ultra-short femtosecond (fs) pulsed laser ablation (PLA) of a zinc plate in deionized water, and are investigated by optical absorption and time resolved luminescence spectra in combination with the morphology and structure analysis. The comparison with previous experiments based on short nanosecond (ns) PLA highlights that pulse duration is a crucial parameter to determine the size and the optical properties of ZnO NPs. While short PLA generates NPs with average size S ‾ of ~ 30 nm, ultrashort PLA allows to achieve much smaller NPs, S ‾ ⩽ 10 nm, that evidence weak quantum confinement effects on both the absorption edge and th…
Controlling the oxidation processes of Zn nanoparticles produced by pulsed laser ablation in aqueous solution
2016
We used online UV-VIS optical absorption and photoluminescence spectra, acquired during and after pulsed laser ablation of a Zinc plate in aqueous solution, to investigate the effect of the laser repetition rate and liquid environment on the oxidation processes of the produced nanoparticles. A transient Zn/ZnO core-shell structure was revealed by the coexistence of an absorption peak around 5.0 eV due to Zn surface plasmon resonance and of an edge at 3.4 eV coming from wurtzite ZnO. The growth kinetics of ZnO at the various repetition rates, selectively probed by the excitonic emission at 3.3 eV, began immediately at the onset of laser ablation and was largely independent of the repetition …
Enhanced optical properties of Cd–Mg-co-doped ZnO nanoparticles induced by low crystal structure distortion
2020
Abstract The growth of CdxMg0.125-xZn0.875O nanoparticles with yellow-orange luminescence is achieved up to 2.5 at. % Cd via a modified sol–gel process. X-ray diffraction analysis confirmed that all the nanoparticles have the hexagonal wurtzite structure. It is found that Cd doping has a considerable effect on the crystal size, microstrain, band gap, and photoluminescence of the Mg0·125Zn0·875O structure, originating from a preferred crystallographic orientation along the (101) plane of the wurtzite structure. The shift and broadening of the E2(high) mode observed in the Raman spectra due to growth-induced strain corroborates the small distortion observed in the X-ray diffraction data. The …
Biocompatibility and Antibacterial Properties of ZnO-Incorporated Anodic Oxide Coatings on TiZrNb Alloy
2020
In a present paper, we demonstrate novel approach to form ceramic coatings with incorporated ZnO nanoparticles (NPs) on low modulus TiZrNb alloy with enhanced biocompatibility and antibacterial parameters. Plasma Electrolytic Oxidation (PEO) was used to integrate ZnO nanoparticles (average size 12&ndash